Effect of Calcium Hydroxide and Antioxidant Agents Filling the Pulp Chamber after Internal Bleaching.

To evaluate the effect of calcium hydroxide (CH), sodium ascorbate (SA) and sodium thiosulfate (ST) filling the pulp chamber on color stability and longevity of teeth after internal bleaching. Crowns of bovine incisors were submitted to internal bleaching and divided into groups according the material used in the pulp chamber: Control, CH, SA, ST. Each group was divided into two subgroups according to the time to perform restorative procedures (7 or 15 days). Color measurement was performed with a spectrophotometer at nine periods. The darkening (ΔE) values were calculated. The Mann-Whitney test was used to statistically analyze the data (p ⟨ 0.05). After bleaching, ΔE values were higher than 3.5, showing that the procedure was effective. After 24 hours, no difference was observed between groups. After 7 days, SA showed higher ΔE than the control group (p ⟨ 0.05). CH and TS did not differ from the control group. In restorations performed after 7/15 days, SA group showed higher values of darkening after 1 and 4 months than the control group (p ⟨ 0.05). SA induced perceptible darkening after bleaching and should not be used to fill the pulp chamber. ST and CH show color stability and longevity after 12 months.

Dual and self-curing potential of self-adhesive resin cements as thin films.

In this study, the dual- and self-curing potential of self-adhesive resin cements (SARCs) as thin, clinically-relevant cement films was investigated. The SARCs tested were: BisCem (BSC; Bisco), Maxcem Elite (MXE; Kerr), RelyX Unicem clicker (UNI; 3M ESPE), seT capsule (SET; SDI), and SmartCem 2 (SC2; Dentsply Caulk). The conventional cement RelyX ARC (3M ESPE) was tested as a reference. The degree of conversion (DC) as a function of time was evaluated by real-time Fourier transform infrared spectroscopy with an attenuated total reflectance (ATR) device. The cements were either photoactivated for 40 seconds (dual-cure mode) or not photoactivated (self-cure mode). The cement film thickness was 50 ± 10 µm. The DC (%) was evaluated 1, 5, 10, 15, 20, 25, and 30 minutes after placing the cement on the ATR cell. Data for DC as a function of time were analyzed by two-way repeated measures analysis of variance (ANOVA). DC values at 30 minutes for the self- and dual-cure modes were submitted to one-way ANOVA. Post hoc comparisons were performed using the Student-Newman-Keuls test (p<0.05). The rate and the extent of conversion were lower for the SARCs compared with the conventional cement. Means ± standard deviations (SD) for the dual-cure mode at 30 minutes were: 75 ± 5 (ARC)a, 73 ± 8 (SET)a, 61 ± 4 (MXE)b, 51 ± 9 (BSC)c, 51 ± 4 (UNI)c, and 48 ± 3 (SC2)c, while in the self-cure mode means and SD were 62 ± 6 (ARC)a, 54 ± 3 (MXE)b, 40 ± 6 (SC2)c, 35 ± 2 (UNI)c, 35 ± 3 (SET)c, and 11 ± 3 (BSC)d. The DC for the dual-cure mode was generally higher than the self-cure, irrespective of the time. Discrepancies in DC between the dual- and self-cure modes from 11% to 79% were observed. In conclusion, SARCs may present slower rate of polymerization and lower final DC than conventional resin cements, in either the dual- or self-cure mode.

Carbamide peroxide bleaching agents: effects on surface roughness of enamel, composite and porcelain.

This study examined the effect of 10 and 35% carbamide peroxide bleaching agents on the surface roughness of enamel, feldspathic porcelain, and microfilled and microhybrid composite resins. Standardized cylindrical specimens were prepared for restorative materials. Enamel samples were obtained from buccal and lingual surfaces of human molars. Samples from each substrate were divided in three subgroups (n=10), according to surface treatment: distilled water (control), and 10 and 35% carbamide peroxide. The 10% agent was applied 3 h daily and the 35% agent was applied for 30 min/week, at 37 degrees C, during 21 days. Control samples remained stored in distilled water, at 37 degrees C. Roughness measurements (Ra, microm) were made at 24 h and repeated after 7, 14 and 21 days of exposure. Data were analyzed using ANOVA (split-plot design) and Tukey's test (5% significance level). Samples from control groups showed no significant alteration during all test periods, while for exposure to 10% agent, only the porcelain presented a rougher surface after 21 days (p<0.05). For the 35% product, roughness means significantly increased during the first and second weeks for enamel (p<0.05), and after 21 days for porcelain (p<0.05) and for the microhybrid composite (p<0.05). Microfilled samples showed no significant alteration throughout the 21-day period, regardless of the surface treatment.